Nominal Voltage: 12 volts (6 cells in series)

Nominal Capacity:
20 hour rate (350mA to 10.50 volts).......7.0 A.H.
10 hour rate (650mA to 10.50 volts).......6.5 A.H.
5 hour rate (1.2A to 10.20 volts).............6.0 A.H.
1 hour rate (4.5A to 9.00 volts)...............4.5 A.H.
15 min rate (14A to 9.00 volts)...............3.5 A.H.

Approximate Weight: 5.70 pounds (2.59 kg)

Energy Density (20 hour rate): 1.43 Watt-hours/cubic inch (87.3 Watt-hours/l)

Specific Energy (20 hour rate) : 14.7 Watt-hours/pound (32.4 Watt-hours/kg)

Internal Resistance (Fully Charged Battery): 22 milliohms (approximately)

Maximum Discharge Current ( ≤ 7 Min.): 21 amperes

Maximum Short-Duration Discharge Current ( ≤ 10 Sec.): 70 amperes

Terminal configurations: Quick disconnect tabs, "F2": 0.250" x 0.032"

Shelf Life - % of nominal capacity at 68° F (20° C):
1 Month: 97%
3 Months: 91%
6 Months: 83%

Operating Temperature Range:
Charge: -4°F (-20°C) to 122°F (50°C)
Discharge: -4°F (-20°C) to 140°F (60°C)

Case: ABS Plastic

Charging Characteristics:

Cycle Applications: Limit initial current to 2.1A. Charge until battery voltage (under charge) reaches 14.40 to 14.70 volts at 68°F (20°C). Hold at 14.40 to 14.70 volts until current drops to approximately 70mA. Battery is fully charged under these conditions, and charger should either be disconnected or switched to "float" voltage.
"Float" or "Stand-By" Service: Hold battery across constant voltage source of 13.50 to 13.80 volts continuously. When held at this voltage, the battery will seek its own current level and maintain itself in a fully charged condition.

NOTE: Due to the self-discharge characteristics of this type of battery, it is imperative that they be charged after 6-9 months of storage, otherwise permanent loss of capacity might occur as a result of sulfation.